    InnovaTest TIME5100 Metal Hardness Tester
    Direct display of hardness values in Rockwell HRB, Rockwell HRC, Vickers HV, Brinell HB, Shore HS and Leeb HLD

    3 Models available 
    TIME5100 - Standard model with integrated impact device D 
    TIME5102 - Special model for Hardness Measurement on surface hardened components, coatings, thin walled components. It has app. 1/4 impact energy of TIME5100/TIME5104. Integrated impact device C. 
    TIME5104 - Special model for Hardness Measurement in extremely confined spaces. Integrated impact device DL. 

    The small portableInnovaTest TIME5100 Metal Hardness Tester is designed for an extremely wide range of applications. They are especially recommended for Hardness Measurement on the shop floor. The automatic identification of the impact test direction makes them easy to use. Hardness tests are possible at any angle, even upside down. The data memory stores up to 270 values. Data can be transferred via USB interface to a computer or printer. 

    The outstanding features of the TH-170 include speedy and exceptionally user-friendly operation and high measuring accuracy, with an extremely low tolerance of ± 1.5%. 

    The hardness tester functions by releasing a small impact device on to the metal testing surface by means of a spring mechanism. The gauge's dynamic measuring procedure works by calculating the difference between the impact velocity and the rebound velocity of impact device. 

    The TH-170 can be used on a whole variety of metals. A statistics program calculates the mean hardness value from a number of single readings. Readings can be printed out immediately on a mini-printer or stored for later processing. 

    Hardness Measurement on metal substances such as: 

    Steel, cast steel, cold work tool steel, stainless steel, grey/nodular cast iron, aluminium, cast aluminium alloys, brass, bronze and wrought copper alloys.


    line
    Kit Contents
    line

    • InnovaTest TIME5100 Metal Hardness Tester
    • Test block with HLD value
    • Charger
    • Cleaning brush
    • Coupling paste
    • Pocket protection case
    • Data cable
    • Manual
    • Certificate
    • Carrying case


    line
    Features
    line

    • Portable dynamic metal hardness testing set
    • Automatic identification of impact test direction
    • Memory up to 270 average readings in 9 freely selectable files
    • Automatic power off
    • Data output USB
    • Integrated impact device: no cables
    • Direct display of hardness values in Rockwell HRB, Rockwell HRC, Vickers HV, Brinell HB, Shore HS and Leeb HLD
    • Test at any angle, even upside down
    • For nearly all metals
    • Upper and lower limit setting
    • Large LCD with backlight
    • Calibration feature


    line
    Specifications
    line

    TIME5100
    Impact deviceD (standard) integrated
    Workpiece radius (convex/concave)Rmin = 50mm (with support ring Rmin = 10mm)
    Workpiece maximum weight2kg on solid support (0.1kg with couplant paste)
    Workpiece min. thickness coupled3mm
    Workpiece min. case hardened depth0.8mm
    TIME5102
    Impact deviceDL integrated
    Workpiece radius (convex/concave)Rmin = 10mm
    Workpiece maximum weight2kg on solid support (0.1kg with couplant paste)
    Workpiece min. thickness coupled3mm
    Workpiece min. case hardened depth0.8mm
    General Information
    Hardness scalesHRC, HRB, HB, HV, HS, HLD
    Measuring rangeHLD 200 to 900
    HRB 13 to 100
    HRC 20 to 68
    HB 20 to 655
    HV 80 to 950
    HS 32 to 100
    Accuracy± 6HLD (for HLD approx. 800)
    Measuring direction0° - 360°
    Memory270 average readings in 9 freely selectable files
    InterfaceUSB 2.0
    Standard impact deviceType D, integrated
    Max. surface roughness of workpiece1.6 µm Ra
    Max. workpiece hardness900 HLD
    Min. workpiece radius (convex/concave)Rmin = 50mm (10mm with support ring)
    Min. workpiece weight2kg on stable support, 0.1kg with coupling paste
    Min. workpiece thickness coupled3mm with coupling paste
    Min. thickness of hardened layers0.8mm
    Power supplyAAA 1.5V batteries (2 pcs)
    Operating temperature0° - 40°C
    Dimensions150 mm x 55 mm x 25 mm
    Weight165 g


    line
    Applications
    line

    • Large, heavy components or fixed machine parts
    • Serial products during the production process
    • Material identification in storage
    • Measurement on locations with difficult access


    line
    Measurement Conditions
    line

    • Minimum measuring area 10 mm x 10 mm
    • Minimum curvature radius r of the measuring area, 30 mm, without adapter.
    • Minimum curvature radius with screw-on V-adapter, 11mm.
    • Samples weighing less than 5 kg and samples less than 5 mm thickshould be placed on a solid base to prevent vibration.
    • Samples weighing less than 2 kg should be fixed to a solid base withcoupling paste


    line
    Related Products
    line

    QH2D
    Portable Leeb Hardness Tester for Steel

    related

    line

    QH5
    Leeb Hardness Tester, Rebound Hardness

    related

    line

    QH7
    Heavy Duty Portable Hardness Tester

    related

    line

    SH-21
    Metal Hardness Tester - Rockwell HRC

    related